The cause of the damage to the high voltage cable 4m

The high voltage cable 4m in the use of X-ray machines is easy to be broken down and damaged, and the repair is also difficult to master. To this end, Newheek summarized the reasons for the failure of high voltage cable 4m as follows
(1) due to long-term dampness or ultraviolet irradiation, rubber aging and lower insulation strength, resulting in breakdown.
(2) the quality of high voltage cable 4m itself is poor, the thickness around the rubber layer and the conductor is uneven, the accidental damage caused by cutting during assembly, the rubber burns during welding, the discharge caused by incomplete cleaning surface, and the welding defects between the conductor and the core and high voltage connector
(3) low insulation strength of filling agent for perfusion, resulting in breakdown.
(4) it is often twisted, hard folded or stressed to break the insulation cracks.
(5) no sudden wave resistance or sudden wave resistance damage, as well as self-rectifying X-ray machine high voltage cable 4m easy to breakdown.
high voltage cable 4m
(6) the rectifying tube is leaky with air and electric leakage short circuit and breakdown.
(7) corroded by gasoline and transformer oil, expanded rubber and reduced insulation breakdown.
In view of the reasons for the damage of the above high voltage cable 4m, some matters should be paid attention to during the maintenance of high voltage cable 4m and methods to prevent further damage in the future.